135˚C CTMS - Heat Shrinkable Identification Sleeves

135˚C CTMS - Heat Shrinkable Identification Sleeves

Applications:
CTMS is made of high-performance polyolefin and is used in industrial, military and aerospace applications. Markers are permanent after printing and do not require an outer protective film.
Approvals / Specifications:
UL224 File no. E255532, 125˚C VW-1
AMS-DTL-23053/5 class 1, SAE-AS81531, MIL-STD-202
Operating Termperature Range:
  • Operating temperature : -55˚C~135˚C
  • Minimum shrink temperature : 70˚C
  • Full recovery temperature: Above 110˚C
Color:

yellow

white

Standard color:Yellow、White
Inquiry
  • Characteristics
  • Specification
  • Technical Data
  • Video
  • Shrink ratio: 3:1
  • Flexible, flame retardant
  • Abrasion and chemical resistance
  • Reliable physical, chemical and electrical performance
  • Flat tubes offer ease of printing
Part NumberNominal SizeAs supplied (mm)After recovered (mm)Standard Length (Meter)
mminchI.D.(min)I.D.(max)
CTMS1353X0024 2.4 3/32 2.4 0.8 100
CTMS1353X0032 3.2 1/8 3.2 1.1 100
CTMS1353X0048 4.8 3/16 4.8 1.6 100
CTMS1353X0064 6.4 1/4 6.4 2.1 100
CTMS1353X0095 9.5 3/8 9.5 3.2 100
CTMS1353X0127 12.7 1/2 12.7 4.2 100
CTMS1353X0191 19.1 3/4 19.1 6.3 100
CTMS1353X0254 25.4 1 25.4 8.5 100
PropertySpecification RequirementTest MethodTypical Value
Longitudinal change 10% ASTM D2671 5%
Tensile strength 10.3MPa ASTM D638 12MPa
Elongation at break 200% ASTM D638 400%
Elongation at break after aging 100% ASTM D638 (175˚C/168 hrs) 400%
Heat shock No cracking ASTM D2671 No cracking
Low temperature flexibility No cracking ASTM D2671 (-55˚C/4 hrs) No cracking
Dielectric voltage withstand AC2500V/60S No breakdown ASTM D2671 No breakdown
Dielectric strength 19。7kV/mm ASTM D2671 25kV/mm
Volume resistivity 1014Ω‧cm ASTM D876 1014Ω‧cm
Copper corrosion No corrosion ASTM D2671 No corrosion
Print performance Print legible after 50 rubs Print legible after 30 strokes SAE AS81531 MIL-STD-202 Pass
Fluid resistance Print legible SAE AS81531 (23˚C/24 hrs) Pass
Flammability Self extinguishing within 1 minute after fire source removed UL224 Pass